262862
钽
wire, diam. 1.0 mm, ≥99.9% trace metals basis
别名:
Ta
登录 查看公司和协议定价
选择尺寸
关于此项目
经验公式（希尔记法）:
Ta
化学文摘社编号:
分子量:
180.95
EC 号:
MDL编号:
UNSPSC代码:
12141741
PubChem化学物质编号:
NACRES:
NA.23
蒸汽压
<0.01 mmHg ( 537.2 °C)
方案
≥99.9% trace metals basis
表单
wire
自燃温度
572 °F
电阻率
13.5 μΩ-cm, 20°C
直径
1.0 mm
沸点
5425 °C (lit.)
mp
2996 °C (lit.)
密度
16.69 g/cm3 (lit.)
SMILES字符串
[Ta]
InChI
1S/Ta
InChI key
GUVRBAGPIYLISA-UHFFFAOYSA-N
制备说明
13g = 1m；65g = 5m
储存分类代码
11 - Combustible Solids
WGK
nwg
闪点(°F)
Not applicable
闪点(°C)
Not applicable
个人防护装备
Eyeshields, Gloves, type N95 (US)
法规信息
新产品
此项目有
Matthew D Budge et al.
Journal of shoulder and elbow surgery, 22(4), 535-541 (2012-09-11)
Aseptic loosening of all-polyethylene glenoid components remains a limiting factor in achieving long-term implant survival in total shoulder arthroplasty (TSA). This study prospectively evaluated the functional and radiographic outcomes of patients undergoing TSA with a novel, porous, tantalum-backed glenoid component
Stuart A Callary et al.
Clinical orthopaedics and related research, 471(7), 2238-2244 (2013-01-22)
One cross-linked polyethylene (XLPE) liner is manufactured using a lower dose of radiation, 5 Mrad, which may result in less cross-linking. The reported in vivo wear rate of this XLPE liner in patients undergoing THA has varied, and has included
Shi-Hua Yu et al.
Water environment research : a research publication of the Water Environment Federation, 84(12), 2115-2122 (2013-01-25)
Tantalum hydroxide exhibits the ability for the removal of phosphate from aqueous solution. The kinetic study, adsorption isotherm, thermodynamic study, desorption, and foreign anions effect were examined in batch experiments. The kinetic process was very well described by a pseudo-second-order
Thomas Larzon et al.
Vascular, 21(2), 87-91 (2013-03-20)
Control of back bleeding from the hypogastric artery into the aneurysm after endovascular aneurysm repair (EVAR) of a ruptured aorto-iliac aneurysm may be necessary in order to avoid a type II endoleak. It is an emergency situation and selective catheterization
Hany A El-Sayed et al.
Nanoscale, 5(4), 1494-1498 (2013-01-23)
Ta oxide nanotubes (NTs) were formed by the anodization of Ta at 15 V in a solution of concentrated sulfuric acid containing 0.8-1.0 M hydrofluoric acid. To study the initial stages of NT formation, FESEM images of samples anodized for
商品
Biomedical implants are essentially foreign substances within the human body that must survive many years’ exposure to demanding mechanical and physiological conditions. Despite these challenges, metal implants have been widely used to substitute for or rebuild hard tissues such as bones and teeth.
我们的科学家团队拥有各种研究领域经验，包括生命科学、材料科学、化学合成、色谱、分析及许多其他领域.
联系客户支持