Photocatalytic decomposition of humic acids in anoxic aqueous solutions producing hydrogen, oxygen and light hydrocarbons.

Photocatalytic decomposition of humic acids in anoxic aqueous solutions producing hydrogen, oxygen and light hydrocarbons.

Environmental technology (2014-08-26)

Deniss Klauson, Olga Budarnaja, Ignacio Castellanos Beltran, Marina Krichevskaya, Sergei Preis

ABSTRACT

Photocatalytic water splitting for hydrogen and oxygen production requires sacrificial electron donors, for example, organic compounds. Titanium dioxide catalysts doped with platinum, cobalt, tungsten, copper and iron were experimentally tested for the production of hydrogen, oxygen and low molecular weight hydrocarbons from aqueous solutions of humic substances (HS). Platinum-doped catalyst showed the best results in hydrogen generation, also producing methane, ethene and ethane, whereas the best oxygen production was exhibited by P25, followed by copper--and cobalt-containing photocatalysts. Iron-containing photocatalyst produced carbon monoxide as a major product. HS undergoing anoxic photocatalytic degradation produce hydrogen with minor hydrocarbons, and/or oxygen. It appears that better hydrogen yield is achieved when direct HS splitting takes place, as opposed to HS acting as electron donors for water splitting.

MATERIALS

Product Number

Brand

Product Description

224227

Sigma-Aldrich

Titanium(IV) oxide, rutile, powder, <5 μm, ≥99.9% trace metals basis

204730

Sigma-Aldrich

Titanium(IV) oxide, rutile, 99.995% trace metals basis

232033

Sigma-Aldrich

Titanium(IV) oxide, anatase, powder, 99.8% trace metals basis

204757

Sigma-Aldrich

Titanium(IV) oxide, rutile, ≥99.98% trace metals basis

460400

Sigma-Aldrich

Titanium, wire, diam. 0.25 mm, 99.7% trace metals basis

248576

Sigma-Aldrich

Titanium(IV) oxide, anatase, powder, −325 mesh, ≥99% trace metals basis

369489

Sigma-Aldrich

Titanium, foil, thickness 2.0 mm, 99.7% trace metals basis

700347

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

637262

Sigma-Aldrich

Titanium(IV) oxide, rutile, nanopowder, <100 nm particle size, 99.5% trace metals basis

637254

Sigma-Aldrich

Titanium(IV) oxide, anatase, nanopowder, <25 nm particle size, 99.7% trace metals basis

635057

Sigma-Aldrich

Titanium(IV) oxide, rutile, <001>, (single crystal substrate), ≥99.9% trace metals basis, L × W × thickness 10 mm × 10 mm × 0.5 mm

634662

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis

GF47404201

Titanium, wire reel, 5m, diameter 0.20mm, annealed, 99.6+%

GF03838282

Titanium, rod, 500mm, diameter 1.5mm, annealed, 99.6+%

GF25290581

Titanium, tube, 1000mm, outside diameter 25.4mm, inside diameter 23.62mm, wall thickness 0.89mm, annealed, 99.6+%

GF10374678

Titanium, rod, 500mm, diameter 5mm, annealed, 99.6+%

GF20882998

Titanium, rod, 200mm, diameter 5mm, annealed, 99.6+%

GF17705516

Titanium, rod, 200mm, diameter 3.0mm, annealed, 99.6+%

GF03916290

Titanium, rod, 490mm, diameter 2mm, annealed, 99.6+%

GF65694426

Titanium, tube, 100mm, outside diameter 1.6mm, inside diameter 1.2mm, wall thickness 0.2mm, hard, 99.6+%

GF12929744

Titanium, microfoil, disks, 25mm, thinness 0.25μm, specific density 112.6μg/cm², permanent mylar 3.5μm support, 99.6+%

GF58567067

Titanium, rod, 100mm, diameter 5mm, annealed, 99.6+%

GF16031843

Titanium, mesh, 100x100mm, nominal aperture 0.19mm, wire diameter 0.23mm, 60x60 wires/inch, open area 20%, twill weave

GF69259315

Titanium, rod, 500mm, diameter 6mm, annealed, 99.6+%

GF72212813

Titanium, tube, 200mm, outside diameter 25.4mm, inside diameter 23.62mm, wall thickness 0.89mm, annealed, 99.6+%

GF61322699

Titanium, rod, 100mm, diameter 2mm, annealed, 99.6+%

GF13915447

Titanium, tube, 100mm, outside diameter 2.03mm, inside diameter 1.55mm, wall thickness 0.24mm, annealed, 99.6+%

GF28411703

Titanium, tube, 100mm, outside diameter 10.3mm, inside diameter 8.7mm, wall thickness 0.8mm, annealed, 99.6+%

GF23916618

Titanium, microfoil, disks, 25mm, thinness 0.5μm, specific density 225.4μg/cm², permanent mylar 3.5μm support, 99.6+%

GF25880485

Titanium, tube, 100mm, outside diameter 6.35mm, inside diameter 5.53mm, wall thickness 0.41mm, annealed, 99.6+%