Enhanced conversion efficiency in dye-sensitized solar cells based on bilayered nano-composite photoanode film consisting of TiO2 nanoparticles and nanofibers.

Enhanced conversion efficiency in dye-sensitized solar cells based on bilayered nano-composite photoanode film consisting of TiO2 nanoparticles and nanofibers.

Journal of nanoscience and nanotechnology (2014-04-18)

P F Du, L X Song, J Xiong

摘要

Novel TiO2 nanoparticles/nanofibers (NPs/NFs) bilayered nano-composite photoanode film for dye-sensitized solar cells (DSSCs) was fabricated through the combination of spin-coating and electrospinning. The NPs and NFs layers have complementary roles. The underlaid spin-coated NPs layer provides the photoanode film with higher specific surface area for dye adsorption and improved adhesion to conductive glass substrate. The overlaid electrospun NFs layer endows the photoanode film with better dye-loading and light-harvesting capabilities due to its porous meshwork structure. And the NFs layer also offers larger pore volume, which can facilitate the electrolyte diffusion and the activity regeneration of dye sensitizers. As a result, the electron transport is accelerated while the charge recombination is suppressed. Ascribing to the synergic effect of the NPs and NFs layers, the TiO2 NPs/NFs-based DSSCs achieve a conversion efficiency of 4.46%, which is nearly 14% higher than that of the pure TiO2 NPs-based ones.

材料

货号

品牌

产品描述

718467

Sigma-Aldrich

氧化钛（IV）, nanopowder, 21 nm primary particle size (TEM), ≥99.5% trace metals basis

637254

Sigma-Aldrich

氧化钛 (IV)，锐钛矿, nanopowder, <25 nm particle size, 99.7% trace metals basis

14027

Sigma-Aldrich

氧化钛（IV）, puriss., meets analytical specification of Ph. Eur., BP, USP, 99-100.5%

232033

Sigma-Aldrich

氧化钛 (IV)，锐钛矿, powder, 99.8% trace metals basis

224227

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, powder, <5 μm, ≥99.9% trace metals basis

14021

Sigma-Aldrich

氧化钛（IV）, ReagentPlus^®, ≥99%

248576

Sigma-Aldrich

氧化钛 (IV)，锐钛矿, powder, −325 mesh, ≥99% trace metals basis

637262

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, nanopowder, <100 nm particle size, 99.5% trace metals basis

634662

Sigma-Aldrich

氧化钛(IV)，金红石和锐钛矿混合物, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis

700347

Sigma-Aldrich

氧化钛(IV)，金红石和锐钛矿混合物, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

204730

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, 99.995% trace metals basis

204757

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, ≥99.98% trace metals basis

677469

Sigma-Aldrich

氧化钛（IV）, contains 1% Mn as dopant, nanopowder, <100 nm particle size (BET), ≥97%

774510

Sigma-Aldrich

氧化钛（IV）, nanowires, diam. × L ~100 nm × 10 μm

774529

Sigma-Aldrich

氧化钛（IV）, nanowires, diam. × L ~10 nm × 10 μm

635057

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, <001>, (single crystal substrate), ≥99.9% trace metals basis, L × W × thickness 10 mm × 10 mm × 0.5 mm

GF16031843

钛, mesh, 100x100mm, nominal aperture 0.19mm, wire diameter 0.23mm, 60x60 wires/inch, open area 20%, twill weave

GF29374005

钛, mesh, 100x100mm, nominal aperture 4.3mm, wire diameter 1.5mm, 4.4x4.4 wires/inch, open area 94%, platinized diamond mesh

348864

Sigma-Aldrich

钛, wire, diam. 0.5 mm, 99.99% trace metals basis

GF34739837

钛, sphere, 200pcs, diameter 3mm, 99.6+%

GF31127712

钛, rod, 10mm, diameter 50mm, 99.99+%

GF66682288

钛, wire reel, 100m, diameter 0.5mm, as drawn, 99.6+%

GF29584187

钛, tube, 500mm, outside diameter 2.03mm, inside diameter 1.55mm, wall thickness 0.24mm, annealed, 99.6+%

GF49264713

钛, tube, 200mm, outside diameter 1.6mm, inside diameter 1.2mm, wall thickness 0.2mm, hard, 99.6+%

GF76772391

钛, rod, 100mm, diameter 10mm, annealed, 99.6+%

GF90963928

钛, rod, 25mm, diameter 50mm, 99.99+%

GF80932822

钛, wire reel, 0.5m, diameter 0.5mm, as drawn, 99.99+%

GF82495198

钛, rod, 200mm, diameter 9.5mm, annealed, 99.99+%

GF46592949

钛, wire, straight, 1000mm, diameter 1.0mm, as drawn, 99.6+%

GF35285384

钛, wire reel, 200m, diameter 0.5mm, as drawn, 99.6+%