Characterisation and thermal properties of titanium dioxide nanoparticles-containing biodegradable polylactide composites synthesized by sol-gel method.

Characterisation and thermal properties of titanium dioxide nanoparticles-containing biodegradable polylactide composites synthesized by sol-gel method.

Journal of nanoscience and nanotechnology (2014-04-18)

Nikiwe Mhlanga, Suprakas Sinha Ray

摘要

This study reports the synthesis, characterisation and thermal properties of polylactide (PLA)/titanium dioxide nanoparticles (TiO2 NPs) composites using the sol-gel method. The percentage weight of TiO2 NP sol was varied from 3, 8, 11 and 14. The synthesised composites were characterised using scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction, energy dispersive X-ray spectroscopy (EDS), thermogravimetric analysis and dynamic mechanical analysis. Encapsulation of the TiO2 into the PLA matrix was attainable based on the SEM images and the FTIR and EDS results. The thermal stability of the composites was shifted to lower temperatures due to photodegradation induced by the metal oxide on the PLA chain. Both PLA and TiO2 NPs have potential in drug delivery because of their biocompatibility and biodegradability.

材料

货号

品牌

产品描述

718467

Sigma-Aldrich

氧化钛（IV）, nanopowder, 21 nm primary particle size (TEM), ≥99.5% trace metals basis

637254

Sigma-Aldrich

氧化钛 (IV)，锐钛矿, nanopowder, <25 nm particle size, 99.7% trace metals basis

14027

Sigma-Aldrich

氧化钛（IV）, puriss., meets analytical specification of Ph. Eur., BP, USP, 99-100.5%

232033

Sigma-Aldrich

氧化钛 (IV)，锐钛矿, powder, 99.8% trace metals basis

224227

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, powder, <5 μm, ≥99.9% trace metals basis

14021

Sigma-Aldrich

氧化钛（IV）, ReagentPlus^®, ≥99%

248576

Sigma-Aldrich

氧化钛 (IV)，锐钛矿, powder, −325 mesh, ≥99% trace metals basis

637262

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, nanopowder, <100 nm particle size, 99.5% trace metals basis

634662

Sigma-Aldrich

氧化钛(IV)，金红石和锐钛矿混合物, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis

700347

Sigma-Aldrich

氧化钛(IV)，金红石和锐钛矿混合物, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

204730

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, 99.995% trace metals basis

204757

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, ≥99.98% trace metals basis

677469

Sigma-Aldrich

氧化钛（IV）, contains 1% Mn as dopant, nanopowder, <100 nm particle size (BET), ≥97%

774510

Sigma-Aldrich

氧化钛（IV）, nanowires, diam. × L ~100 nm × 10 μm

774529

Sigma-Aldrich

氧化钛（IV）, nanowires, diam. × L ~10 nm × 10 μm

635057

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, <001>, (single crystal substrate), ≥99.9% trace metals basis, L × W × thickness 10 mm × 10 mm × 0.5 mm

GF16031843

钛, mesh, 100x100mm, nominal aperture 0.19mm, wire diameter 0.23mm, 60x60 wires/inch, open area 20%, twill weave

GF29374005

钛, mesh, 100x100mm, nominal aperture 4.3mm, wire diameter 1.5mm, 4.4x4.4 wires/inch, open area 94%, platinized diamond mesh

348864

Sigma-Aldrich

钛, wire, diam. 0.5 mm, 99.99% trace metals basis

GF34739837

钛, sphere, 200pcs, diameter 3mm, 99.6+%

GF31127712

钛, rod, 10mm, diameter 50mm, 99.99+%

GF66682288

钛, wire reel, 100m, diameter 0.5mm, as drawn, 99.6+%

GF29584187

钛, tube, 500mm, outside diameter 2.03mm, inside diameter 1.55mm, wall thickness 0.24mm, annealed, 99.6+%

GF49264713

钛, tube, 200mm, outside diameter 1.6mm, inside diameter 1.2mm, wall thickness 0.2mm, hard, 99.6+%

GF76772391

钛, rod, 100mm, diameter 10mm, annealed, 99.6+%

GF90963928

钛, rod, 25mm, diameter 50mm, 99.99+%

GF80932822

钛, wire reel, 0.5m, diameter 0.5mm, as drawn, 99.99+%

GF82495198

钛, rod, 200mm, diameter 9.5mm, annealed, 99.99+%

GF46592949

钛, wire, straight, 1000mm, diameter 1.0mm, as drawn, 99.6+%

GF35285384

钛, wire reel, 200m, diameter 0.5mm, as drawn, 99.6+%