Fabrication of ordered poly(methyl methacrylate) nanobowl arrays using SiO2 colloidal crystal templates.

Fabrication of ordered poly(methyl methacrylate) nanobowl arrays using SiO2 colloidal crystal templates.

Journal of nanoscience and nanotechnology (2014-04-18)

Lier Deng, Ming Fu, Yinglei Tao, Xiaoyun Guo

摘要

A simple approach is presented for the fabrication of poly(methyl methacrylate) (PMMA) nanobowl arrays over cm2 areas using SiO2 colloidal crystal templates. SiO2 colloidal crystal templates were prepared on a clean glass substrate by self-assembled SiO2 spheres of 410 nm in diameter. The air between the silica spheres was filled by the superfluous monomer of PMMA that can be subsequently polymerized. After infiltration, the SiO2-PMMA templates were immersed in a 3 wt% hydrofluoric acid (HF) aqueous solution. After 24 h, silica spheres were etched and a free-standing nanobowl sheet was obtained. The size of the nanobowls could be controlled by the size of the SiO2 spheres and the area of the nanobowl sheet could be altered by the size of the glass substrate.

材料

货号

品牌

产品描述

Sigma-Aldrich

聚甲基丙烯酸甲酯

Sigma-Aldrich

聚甲基丙烯酸甲酯, average M_w ~350,000 by GPC

Sigma-Aldrich

二氧化硅, nanopowder, 10-20 nm particle size (BET), 99.5% trace metals basis

Sigma-Aldrich

LUDOX ^® AS-40 胶态二氧化硅, 40 wt. % suspension in H₂O

Sigma-Aldrich

LUDOX^® HS-40胶态氧化硅, 40 wt. % suspension in H₂O

Sigma-Aldrich

聚甲基丙烯酸甲酯

Sigma-Aldrich

二氧化硅, nanopowder (spherical, porous), 5-20 nm particle size (TEM), 99.5% trace metals basis

Sigma-Aldrich

聚甲基丙烯酸甲酯, average M_w ~15,000 by GPC, powder

Sigma-Aldrich

LUDOX^® TM-50 胶态氧化硅, 50 wt. % suspension in H₂O

Sigma-Aldrich

二氧化硅, nanoparticles, mesoporous, 200 nm particle size, pore size 4 nm

Sigma-Aldrich

二氧化硅, nanopowder, 99.8% trace metals basis

Sigma-Aldrich

介孔结构的二氧化硅, MCM-41 type (hexagonal)

Sigma-Aldrich

二氧化硅

Sigma-Aldrich

LUDOX ^® TMA 胶态二氧化硅, 34 wt. % suspension in H₂O

Sigma-Aldrich

LUDOX ^® AS-30 胶态二氧化硅, 30 wt. % suspension in H₂O

Sigma-Aldrich

LUDOX ^® HS-30 胶态二氧化硅, 30 wt. % suspension in H₂O

Sigma-Aldrich

LUDOX ^® TM-40 胶态二氧化硅, 40 wt. % suspension in H₂O

Sigma-Aldrich

LUDOX^®SM胶体二氧化硅, 30 wt. % suspension in H₂O

Sigma-Aldrich

LUDOX ^® AM 胶态二氧化硅, 30 wt. % suspension in H₂O

Sigma-Aldrich

LUDOX^® LS 胶态氧化硅, 30 wt. % suspension in H₂O

Sigma-Aldrich

LUDOX^® CL 胶态氧化硅, 30 wt. % suspension in H₂O

Supelco

聚甲基丙烯酸甲酯, analytical standard, for GPC, 2,000

Supelco

聚甲基丙烯酸甲酯, analytical standard, for GPC, 100,000

Supelco

聚甲基丙烯酸甲酯, analytical standard, for GPC, 10,000

Supelco

聚甲基丙烯酸甲酯, analytical standard, for GPC, 2,480,000

Sigma-Aldrich

介孔结构的二氧化硅, MSU-F (cellular foam)

Supelco

聚甲基丙烯酸甲酯, analytical standard, for GPC, average M_w 97,000 (Typical), average M_n 46,000 (Typical)

Supelco

聚甲基丙烯酸甲酯, analytical standard, for GPC, 4,000

Sigma-Aldrich

LUDOX^® CL-X 胶态氧化硅, 45 wt. % suspension in H₂O

Supelco

聚甲基丙烯酸甲酯, analytical standard, for GPC, 20,000