grade
electrophoresis grade
vapor density
5.31 (vs air)
assay
≥99%
mp
>300 °C (lit.)
solubility
H2O: soluble 20 g/L at 20 °C
SMILES string
C=CC(=O)NCNC(=O)C=C
InChI
1S/C7H10N2O2/c1-3-6(10)8-5-9-7(11)4-2/h3-4H,1-2,5H2,(H,8,10)(H,9,11)
InChI key
ZIUHHBKFKCYYJD-UHFFFAOYSA-N
General description
N,N′-Methylenebis(acrylamide) is a cross linking agent that polymerizes with acrylamide and creates cross links within the polyacrylamide gel. It is capable of creating a network rather than linear chains which helps in maintaining the firmness of gel.
Application
N,N′-Methylenebis(acrylamide) has been used for synthesis of polymerized crystalline colloidal array (PCCAs). It has also been used for gel preparation.
Still not finding the right product?
Explore all of our products under N,N′-亚甲基双丙烯酰胺
signalword
Danger
Hazard Classifications
Acute Tox. 3 Oral - Acute Tox. 4 Dermal - Carc. 1B - Muta. 1B - Repr. 2 - STOT RE 1 Oral
target_organs
Peripheral nervous system
存储类别
6.1C - Combustible acute toxic Cat.3 / toxic compounds or compounds which causing chronic effects
wgk
WGK 3
flash_point_f
Not applicable
flash_point_c
Not applicable
ppe
dust mask type N95 (US), Eyeshields, Faceshields, Gloves
法规信息
新产品
此项目有
Timothy Olding et al.
Journal of medical physics, 36(1), 3-14 (2011-03-25)
This paper explores the combination of cone beam optical computed tomography with an N-isopropylacrylamide (NIPAM)-based polymer gel dosimeter for three-dimensional dose imaging of small field deliveries. Initial investigations indicate that cone beam optical imaging of polymer gels is complicated by
Roongnapa Suedee et al.
Journal of chromatography. A, 1114(2), 239-249 (2006-03-15)
A temperature sensitive dopamine-imprinted polymer was prepared in 80% aqueous methanol solution by free-radical cross-linking co-polymerisation of methacrylic acid and acrylamide at 60 degrees C in the presence of N,N-methylene-bis-acrylamide as the cross-linker and dopamine hydrochloride as template molecule. The
Yan Lu et al.
ACS nano, 4(12), 7078-7086 (2010-11-19)
Here, we demonstrate that bimetallic Au-Pt nanorods (NRs) can be grown in situ into thermosensitive core-shell microgel particles by a novel two-step approach. In the first step, Au NRs with an average width of 6.6 ± 0.3 nm and length