Product Name
碳纳米管，单壁，聚乙二醇官能化, >80% carbon basis, D × L 4-5 nm × 0.5-0.6 μm , bundle dimensions, avg. no. of layers, 1
方案
>80% carbon basis
表单
powder
分子量
Mw ~600 g/mol (PEG)
特点
avg. no. of layers 1
直径 × 长度
4-5 nm × 0.5-0.6 μm , bundle dimensions
杂质
4-5% trace metals
溶解性
H2O: 5 mg/mL
官能团
PEG
制备说明
Electric Arc Discharge Method
Procedure for dispersion of this PEG-functionalized SWNTs product in water:
Typically after this procedure, the material is completely dispersed according to visual observation.
Sonicate 50 mg of material in 5 mL water for 30 min. (A bath sonicator with a sonic power between 45 W and 270 W works fine. A sonic power of 270 W is preferable for faster dispersion).
Add 45 mL of water and sonicate for additional 60 min (or until the material appears well-dispersed).
Dilute the dispersion to the desired concentration and sonicate if necessary. If aggregates are still visible continue to sonicate until satisfactory dispersion is obtained. Note: If unable to achieve a satisfactory dispersion, reduce the initial amount of 50 mg of material in 5 mL of water.
This procedure is to be used as a basis and additional procedures can be researched. Results may vary if this is the first time working with this material. Solubility of this PEG-functionalized SWNTs product can reach 5.0 mg/mL in water.
Typically after this procedure, the material is completely dispersed according to visual observation.
Sonicate 50 mg of material in 5 mL water for 30 min. (A bath sonicator with a sonic power between 45 W and 270 W works fine. A sonic power of 270 W is preferable for faster dispersion).
Add 45 mL of water and sonicate for additional 60 min (or until the material appears well-dispersed).
Dilute the dispersion to the desired concentration and sonicate if necessary. If aggregates are still visible continue to sonicate until satisfactory dispersion is obtained. Note: If unable to achieve a satisfactory dispersion, reduce the initial amount of 50 mg of material in 5 mL of water.
This procedure is to be used as a basis and additional procedures can be researched. Results may vary if this is the first time working with this material. Solubility of this PEG-functionalized SWNTs product can reach 5.0 mg/mL in water.
分析说明
按 Nano Letters, 2003, 3(3), 309-314 中所述测定含碳量。
警示用语：
Warning
危险声明
危险分类
Eye Irrit. 2 - STOT SE 3
靶器官
Respiratory system
储存分类代码
11 - Combustible Solids
WGK
WGK 3
闪点(°F)
Not applicable
闪点(°C)
Not applicable
个人防护装备
dust mask type N95 (US), Eyeshields, Gloves
我们的科学家团队拥有各种研究领域经验，包括生命科学、材料科学、化学合成、色谱、分析及许多其他领域.
联系客户支持