Surface plasmon-enhanced light-emission mechanism of Ag-coated ZnO/Al2O3 core/shell nanorod structures.

Surface plasmon-enhanced light-emission mechanism of Ag-coated ZnO/Al2O3 core/shell nanorod structures.

Journal of nanoscience and nanotechnology (2013-07-19)

Bum-Young Noh, Seong-Ho Baek, Yong-Il Jung, Jae Hyun Kim, Il-Kyu Park

摘要

Surface plasmon (SP)-enhanced light emission mechanism has been investigated for the Ag-coated ZnO/Al2O3 core/shell nanorods (NRs). Structural characterizations showed that the ZnO NRs were covered by conformal Al2O3 layer and coated by Ag nanoparticles (NPs). The optical studies by photoluminescence (PL) showed abnormal variation of PL intensity with increasing the thickness of Al2O3. For the Ag NPs-coated ZnO NRs without Al2O3 shell layer, the PL emission quenched due to direct transfer of the photo-excited electrical carriers from ZnO NRs to Ag NPs. With thin Al2O3 layers less than 15 nm, the PL intensity increased with increasing the thickness of Al2O3 layers due to weakening of the Förster-type energy transfer while strong SP-mediated PL emission enhancement. For thicker Al2O3 layers than 15 nm, however, the PL intensity decreased with increasing the thickness of Al2O3 layers due to weakening of SP-mediated PL emission enhancement.

材料

Product Number

品牌

产品描述

Sigma-Aldrich

氧化铝, standard grade, Brockmann I, activated, basic

Sigma-Aldrich

氧化铝, activated, Brockmann I, standard grade, neutral

Sigma-Aldrich

氧化锌, ReagentPlus^®, powder, <5 μm particle size, 99.9%

Sigma-Aldrich

氧化铝, powder, primarily α phase, ≤10 μm avg. part. size, 99.5% trace metals basis

Sigma-Aldrich

氧化锌, puriss. p.a., ACS reagent, ≥99.0% (KT)

Sigma-Aldrich

氧化锌, nanopowder, <100 nm particle size

Sigma-Aldrich

氧化铝, Brockmann I, standard grade, activated, acidic

Sigma-Aldrich

氧化铝, nanopowder, <50 nm particle size (TEM)

Sigma-Aldrich

氧化铝, powder, 99.99% trace metals basis

Sigma-Aldrich

氧化锌, nanopowder, <50 nm particle size (BET), >97%

Sigma-Aldrich

氧化锌，分散体, nanoparticles, <100 nm particle size (TEM), ≤40 nm avg. part. size (APS), 20 wt. % in H₂O

Sigma-Aldrich

氧化铝, nanoparticles, <50 nm particle size (DLS), 20 wt. % in isopropanol

Sigma-Aldrich

氧化铝, nanopowder, 13 nm primary particle size (TEM), 99.8% trace metals basis

Sigma-Aldrich

氧化铝, fused, powder, primarily α-phase, -325 mesh

Sigma-Aldrich

氧化锌, puriss., meets analytical specification of Ph. Eur., BP, USP, 99-100.5% (calc. for dried substance)

Sigma-Aldrich

氧化铝, pellets, 3 mm

Sigma-Aldrich

氧化铝, Corundum, α-phase, -100 mesh

Supelco

氧化铝, activated, neutral, Brockmann Activity I

Sigma-Aldrich

氧化锌, 99.99% trace metals basis

Sigma-Aldrich

氧化铝, pore size 58 Å, ~150 mesh

Sigma-Aldrich

氧化铝, fused, powder, primarily α-phase, 100-200 mesh

Sigma-Aldrich

氧化铝, Type WN-6, Neutral, Activity Grade Super I

Sigma-Aldrich

氧化铝, nanoparticles, 30-60 nm particle size (TEM), 20 wt. % in H₂O

Sigma-Aldrich

金, powder, <45 μm, 99.99% trace metals basis

Sigma-Aldrich

氧化铝, 99.997% trace metals basis

Sigma-Aldrich

氧化铝, single crystal substrate, <0001>

Sigma-Aldrich

氧化锌, 99.999% trace metals basis

Sigma-Aldrich

氧化铝, Brockmann I, standard grade, activated, neutral, free-flowing, Redi-Dri^™

Sigma-Aldrich

镀金显微镜载片, layer thickness 1000 Å, 99.999% (Au)

Sigma-Aldrich

氧化铝, nanowires, diam. × L 2-6 nm × 200-400 nm