Al3+ ions dependent structural and magnetic properties of Co-Ni nano-alloys.

Al3+ ions dependent structural and magnetic properties of Co-Ni nano-alloys.

Journal of nanoscience and nanotechnology (2014-04-18)

R H Kadam, Suresh T Alone, Anil S Gaikwad, A P Birajdar, Sagar E Shirsath

摘要

Ferrite samples with a chemical formula Co0.5Ni0.5Al(x)Fe(2-x)O4 (where x = 0.0, 0.25, 0.5, 0.75 and 1.0) were synthesized by sol-gel auto-combustion method. The synthesized samples were annealed at 600 degrees C for 4 h. An analysis of X-ray diffraction (XRD) patterns reveals the formation of single phase cubic spinel structure. The lattice parameter decreased linearly with the increasing Al content x. Nano size of the powders were confirmed by the transmission electron micrographs (TEM). Particle size, bulk density decreased whereas specific surface area and porosity of the samples increased with the Al substitution. Cation distribution of constituent ions shows linear dependence of Al substitution. Based on the cation distribution obtained from XRD data, structural parameters such as lattice parameters, ionic radii of available sites and the oxygen parameter 'u' is calculated. Saturation magnetization (M(s)), magneton number (n(B)) and coercivity (H(c)) decreased with the Al substitution. Possible explanation for the observed structural and magnetic behavior with various Al content are discussed.

材料

Product Number

品牌

产品描述

Sigma-Aldrich

钴, powder, 2 μm particle size, 99.8% trace metals basis

Sigma-Aldrich

Raney^®-镍, W.R. Grace and Co. Raney^® 2400, slurry, in H₂O, active catalyst

Sigma-Aldrich

镍, powder, <150 μm, 99.99% trace metals basis

镍, rod, 100mm, diameter 1.5mm, 99.99+%

Sigma-Aldrich

镍, foil, thickness 0.5 mm, 99.98% trace metals basis

Sigma-Aldrich

铝, foil, thickness 0.45-0.55 mm, 99.999% trace metals basis

Sigma-Aldrich

钴, granular, 99.99% trace metals basis

Sigma-Aldrich

镍, powder, <1 μm, 99.8% trace metals basis

Sigma-Aldrich

镍, wire, diam. 0.25 mm, ≥99.9%

Sigma-Aldrich

铝, foil, thickness 0.13 mm, ≥99.99% trace metals basis

Sigma-Aldrich

钴, Carbon coated magnetic, nanopowder, <50 nm particle size (TEM), ≥99%

Sigma-Aldrich

铝, foil, thickness 8 μm, 99% trace metals basis

Sigma-Aldrich

钴, pieces, 99.5% trace metals basis

Sigma-Aldrich

镍, rod, diam. 6.35 mm, ≥99.99% trace metals basis

Sigma-Aldrich

铝, wire, diam. 0.58 mm, ≥99.99% trace metals basis

镍, pellets, 100g, max. size 10mm, 99.999%

Sigma-Aldrich

镍, wire, diam. 0.5 mm, ≥99.9% trace metals basis

镍, mesh, 30x30mm, nominal aperture 0.34mm, thickness 0.025mm, wire diameter 0.041mm, 70 wires/inch, open area 80%, electro-formed mesh, 99.9%

Sigma-Aldrich

钴, wire, diam. 1.0 mm, 99.995% trace metals basis

Sigma-Aldrich

镍, wire, diam. 0.5 mm, ≥99.99% trace metals basis

Sigma-Aldrich

铝, evaporation slug, diam. × L 6.3 mm × 6.3 mm, 99.999% trace metals basis

Sigma-Aldrich

镍, foil, thickness 0.1 mm, 99.98% trace metals basis

Sigma-Aldrich

镍, sputtering target, diam. × thickness 2.00 in. × 0.25 in., 99.95% trace metals basis

铝, tube, 200mm, outside diameter 3.0mm, inside diameter 1.62mm, wall thickness 0.69mm, hard, 99.5%

Sigma-Aldrich

镍, foil, thickness 0.25 mm, 99.995% trace metals basis

铝, rod, 1000mm, diameter 12.7mm, 99%

镍, foil, 100x100mm, thickness 1.6mm, 99%

Sigma-Aldrich

钴, foil, thickness 0.1 mm, 99.95% trace metals basis

Sigma-Aldrich

钴, foil, thickness 1.0 mm, 99.95% trace metals basis

镍, foil, light tested, 150x150mm, thickness 0.025mm, 99.9%