  • Pullulan/dextran/nHA macroporous composite beads for bone repair in a femoral condyle defect in rats.

Pullulan/dextran/nHA macroporous composite beads for bone repair in a femoral condyle defect in rats.

PloS one (2014-10-21)
Silke Schlaubitz, Sidi Mohammed Derkaoui, Lydia Marosa, Sylvain Miraux, Martine Renard, Sylvain Catros, Catherine Le Visage, Didier Letourneur, Joëlle Amédée, Jean-Christophe Fricain
摘要

The repair of bone defects is of particular interest for orthopedic, oral, maxillofacial, and dental surgery. Bone loss requiring reconstruction is conventionally addressed through bone grafting. Depending on the size and the location of the defect, this method has limits and risks. Biomaterials can offer an alternative and have features supporting bone repair. Here, we propose to evaluate the cellular penetration and bone formation of new macroporous beads based on pullulan/dextran that has been supplemented with nanocrystalline hydroxyapatite in a rat model. Cross-linked beads of 300-500 µm diameters were used in a lateral femoral condyle defect and analyzed by magnetic resonance imaging, micro-computed tomography, and histology in comparison to the empty defects 15, 30, and 70 days after implantation. Inflammation was absent for both conditions. For empty defects, cellularisation and mineralization started from the periphery of the defect. For the defects containing beads, cellular structures filling out the spaces between the scaffolds with increasing interconnectivity and trabecular-like organization were observed over time. The analysis of calcified sections showed increased mineralization over time for both conditions, but was more pronounced for the samples containing beads. Bone Mineral Density and Bone Mineral Content were both significantly higher at day 70 for the beads in comparison to empty defects as well as compared with earlier time points. Analysis of newly formed tissue around the beads showed an increase of osteoid tissue, measured as percentage of the defect surface. This study suggests that the use of beads for the repair of small size defects in bone may be expanded on to meet the clinical need for a ready-to-use fill-up material that can favor bone formation and mineralization, as well as promote vessel ingrowth into the defect site.

材料
货号
品牌
产品描述

Sigma-Aldrich
磷酸, ACS reagent, ≥85 wt. % in H2O
Sigma-Aldrich
磷酸, 85 wt. % in H2O, 99.99% trace metals basis
Sigma-Aldrich
甲基丙烯酸甲酯, contains ≤30 ppm MEHQ as inhibitor, 99%
Sigma-Aldrich
磷酸, ACS reagent, ≥85 wt. % in H2O
Sigma-Aldrich
氢氧化钙, ACS reagent, ≥95.0%
Sigma-Aldrich
磷酸, crystalline, ≥99.999% trace metals basis
Sigma-Aldrich
磷酸, BioUltra, ≥85% (T)
Sigma-Aldrich
苯甲酸甲酯, 99%
Sigma-Aldrich
磷酸, puriss. p.a., ACS reagent, reag. ISO, reag. Ph. Eur., ≥85%
Sigma-Aldrich
磷酸 溶液, 85 wt. % in H2O, FCC, FG
Sigma-Aldrich
甲基丙烯酸丁酯, 99%, contains monomethyl ether hydroquinone as inhibitor
Sigma-Aldrich
磷酸, puriss. p.a., crystallized, ≥99.0% (T)
Sigma-Aldrich
磷酸, puriss., meets analytical specification of Ph. Eur., BP, NF, FCC, 85.0-88.0%
Sigma-Aldrich
甲基丙烯酸甲酯, 99%, stabilized
Sigma-Aldrich
磷酸, ≥85 wt. % in H2O, ≥99.999% trace metals basis
Sigma-Aldrich
磷酸, BioReagent, suitable for insect cell culture, 85%
Supelco
苯甲酸甲酯, analytical standard
Sigma-Aldrich
氢氧化钙, 99.995% trace metals basis
Sigma-Aldrich
4,N,N-三甲基苯胺, 99%
Sigma-Aldrich
磷酸 溶液, NMR reference standard, 85% in D2O (99.9 atom % D), NMR tube size 4.2 mm × 8 in. , WGS-5BL Coaxial NMR tube
甲基丙烯酸甲酯, European Pharmacopoeia (EP) Reference Standard
异氟醚, European Pharmacopoeia (EP) Reference Standard
Sigma-Aldrich
苯甲酸甲酯, natural, ≥98%, FCC, FG
Sigma-Aldrich
苯甲酸甲酯, ≥98%, FCC, FG
甲基丙烯酸丁酯, European Pharmacopoeia (EP) Reference Standard
Sigma-Aldrich
4,N,N-三甲基苯胺, catalyst grade (for peroxide polymerization), ≥98.5% (GC)
Sigma-Aldrich
磷酸 溶液, NMR reference standard, 85% in D2O (99.9 atom % D), NMR tube size 5 mm × 8 in.
Sigma-Aldrich
磷酸 溶液, NMR reference standard, 85% in D2O (99.9 atom % D), NMR tube size 3 mm × 8 in.
Sigma-Aldrich
4,N,N-三甲基苯胺, purum, ≥98.0% (GC)
Sigma-Aldrich
磷酸-16O4 溶液, 70 wt. % in D2O, 99.9 atom % 16O