Electrochemical degradation of nitrobenzene by anodic oxidation on the constructed TiO2-NTs/SnO2-Sb/PbO2 electrode.

Electrochemical degradation of nitrobenzene by anodic oxidation on the constructed TiO2-NTs/SnO2-Sb/PbO2 electrode.

Chemosphere (2014-07-30)

Yong Chen, Hongyi Li, Weijing Liu, Yong Tu, Yaohui Zhang, Weiqing Han, Lianjun Wang

摘要

The interlayer of Sb-doped SnO2 (SnO2-Sb) and TiO2 nanotubes (TiO2-NTs) on Ti has been introduced into the PbO2 electrode system with the aim to reveal the mechanism of enhanced electrochemical performance of TiO2-NTs/SnO2-Sb/PbO2 electrode. In contrast with the traditional Ti/SnO2-Sb/PbO2 electrode, the constructed PbO2 electrode has a more regular and compact morphology with better oriented crystals of lower size. The TiO2-NTs/SnO2-Sb interlayer prepared by electrodeposition process improves PbO2 coating structure effectively, and enhances the electrochemical performance of PbO2 electrode. Kinetic analyses indicated that the electrochemical oxidation of nitrobenzene on the PbO2 electrodes followed pseudo-first-order reaction, and mass transport was enhanced at the constructed electrode. The accumulation of nitrocompounds of degradation intermediates on constructed electrode was lower, and almost all of the nitro groups were eliminated from aromatic rings after 6h of electrolysis. Higher combustion efficiency was obtained on the constructed TiO2-NTs/SnO2-Sb/PbO2 electrode. The intermediates of nitrobenzene oxidation were confirmed by IC and GC/MS.

材料

货号

品牌

产品描述

718467

Sigma-Aldrich

氧化钛（IV）, nanopowder, 21 nm primary particle size (TEM), ≥99.5% trace metals basis

637254

Sigma-Aldrich

氧化钛 (IV)，锐钛矿, nanopowder, <25 nm particle size, 99.7% trace metals basis

252379

Sigma-Aldrich

硝基苯, ACS reagent, ≥99.0%

14027

Sigma-Aldrich

氧化钛（IV）, puriss., meets analytical specification of Ph. Eur., BP, USP, 99-100.5%

232033

Sigma-Aldrich

氧化钛 (IV)，锐钛矿, powder, 99.8% trace metals basis

224227

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, powder, <5 μm, ≥99.9% trace metals basis

14021

Sigma-Aldrich

氧化钛（IV）, ReagentPlus^®, ≥99%

248576

Sigma-Aldrich

氧化钛 (IV)，锐钛矿, powder, −325 mesh, ≥99% trace metals basis

637262

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, nanopowder, <100 nm particle size, 99.5% trace metals basis

634662

Sigma-Aldrich

氧化钛(IV)，金红石和锐钛矿混合物, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis

N10950

Sigma-Aldrich

硝基苯, ReagentPlus^®, 99%

391352

Sigma-Aldrich

铅, powder, −100 mesh, 99.95% trace metals basis

700347

Sigma-Aldrich

氧化钛(IV)，金红石和锐钛矿混合物, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

204730

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, 99.995% trace metals basis

204757

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, ≥99.98% trace metals basis

677469

Sigma-Aldrich

氧化钛（IV）, contains 1% Mn as dopant, nanopowder, <100 nm particle size (BET), ≥97%

GF05266672

铅, rod, 100mm, diameter 19.0mm, 99.95%

06084

Supelco

硝基苯, PESTANAL^®, analytical standard

396117

Sigma-Aldrich

铅, shot, <2 mm, 99.9% trace metals basis

774510

Sigma-Aldrich

氧化钛（IV）, nanowires, diam. × L ~100 nm × 10 μm

209708

Sigma-Aldrich

铅, powder, −325 mesh, ≥99% trace metals basis

695912

Sigma-Aldrich

铅, shot, 1-3 mm, 99.995% trace metals basis

40054

Supelco

硝基苯溶液, certified reference material, 5000 μg/mL in methanol

774529

Sigma-Aldrich

氧化钛（IV）, nanowires, diam. × L ~10 nm × 10 μm

635057

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, <001>, (single crystal substrate), ≥99.9% trace metals basis, L × W × thickness 10 mm × 10 mm × 0.5 mm

GF16031843

钛, mesh, 100x100mm, nominal aperture 0.19mm, wire diameter 0.23mm, 60x60 wires/inch, open area 20%, twill weave

GF29374005

钛, mesh, 100x100mm, nominal aperture 4.3mm, wire diameter 1.5mm, 4.4x4.4 wires/inch, open area 94%, platinized diamond mesh

GF68213538

铅, foil, 100x100mm, thickness 0.125mm, as rolled, 99.95%

GF92060489

铅, rod, 1000mm, diameter 3.2mm, 99.95%

348864

Sigma-Aldrich

钛, wire, diam. 0.5 mm, 99.99% trace metals basis