Fabrication of strongly attached hydroxyapatite coating on titanium by hydrothermal treatment of Ti-Zn-PO4 coated titanium in CaCl 2 solution.

Journal of materials science. Materials in medicine (2015-07-17)
Alireza Valanezhad, Kanji Tsuru, Kunio Ishikawa
PMID26178647
摘要

Hydroxyapatite (HAp) coating was formed on zinc phosphate (Ti-Zn-PO4) coated Ti plates by hydrothermal treatment in CaCl2 solution at 200 °C for 12 h. Uniform surface coverage of the fabricated HAp coating was obtained by this method. SEM-EDX analysis of the adhesion test area showed that the presence of fractures only occurred in HAp crystals. On the other words cohesive fracture was seen in HAp coating layer formed on the Ti-Zn-PO4. The measured strength was around 42.3 ± 17 MPa. Rat bone marrow (RBM) mesenchymal stem cells were cultured and differentiation-induced on each sample (Ti plate, Ti-Zn-PO4 coated and HAp coated), and cell calcification properties were examined. Apparent differences in morphology and extension of the RBM cells were obtained, while the Ti-Zn-PO4 coated samples showed the highest cell number among all samples. After differentiation-induction, HAp coated samples showed the highest amount of alkaline phosphatase activity, and the highest level of cell calcification. Therefore, the hard tissue compatibility of Ti is improved by hydrothermally HAp coating of samples.

材料
产品编号
品牌
产品描述
D4902
Sigma-Aldrich
地塞米松, powder, BioReagent, suitable for cell culture, ≥97%
225711
Sigma-Aldrich
硝酸, 70%, purified by redistillation, ≥99.999% trace metals basis
A4403
Sigma-Aldrich
L -抗坏血酸, powder, suitable for cell culture, γ-irradiated
21115
Sigma-Aldrich
氯化钙 溶液, BioUltra, Molecular Biology, ~1 M in H2O
A5960
Sigma-Aldrich
L -抗坏血酸, BioXtra, ≥99.0%, crystalline
A4544
Sigma-Aldrich
L -抗坏血酸, suitable for cell culture, suitable for plant cell culture, ≥98%
A92902
Sigma-Aldrich
L -抗坏血酸, 99%
G5882
Sigma-Aldrich
戊二醛 溶液, Grade I, 25% in H2O, specially purified for use as an electron microscopy fixative
A7506
Sigma-Aldrich
L -抗坏血酸, reagent grade, crystalline
C5670
Sigma-Aldrich
氯化钙, anhydrous, BioReagent, suitable for insect cell culture, suitable for plant cell culture, ≥96.0%
G6257
Sigma-Aldrich
戊二醛 溶液, Grade II, 25% in H2O
340855
Sigma-Aldrich
戊二醛 溶液, 50 wt. % in H2O
255564
Sigma-Aldrich
L -抗坏血酸, ACS reagent, ≥99%
499609
Sigma-Aldrich
氯化钙, powder, 99.99% trace metals basis
A2218
Sigma-Aldrich
L -抗坏血酸, meets USP testing specifications
A0278
Sigma-Aldrich
L -抗坏血酸, reagent grade
C8106
Sigma-Aldrich
氯化钙
G7651
Sigma-Aldrich
戊二醛 溶液, Grade I, 50% in H2O, specially purified for use as an electron microscopy fixative or other sophisticated use
695041
Sigma-Aldrich
硝酸, ACS reagent, ≥90.0%
33034
Sigma-Aldrich
L -抗坏血酸, puriss. p.a., ACS reagent, reag. ISO, Ph. Eur., 99.7-100.5% (oxidimetric)
W210901
Sigma-Aldrich
L -抗坏血酸, FCC, FG
449709
Sigma-Aldrich
氯化钙, AnhydroBeads™, −10 mesh, ≥99.9% trace metals basis
G7776
Sigma-Aldrich
戊二醛 溶液, Grade I, 70% in H2O, specially purified for use as an electron microscopy fixative or other sophisticated use
95209
Sigma-Aldrich
L -抗坏血酸, BioUltra, ≥99.5% (RT)
W512303
Sigma-Aldrich
戊二醛 溶液, 50 wt. % in H2O, FCC
G7526
Sigma-Aldrich
戊二醛 溶液, Grade I, 8% in H2O, specially purified for use as an electron microscopy fixative or other sophisticated use
G6403
Sigma-Aldrich
戊二醛 溶液, 50% in H2O, suitable for photographic applications
95210
Sigma-Aldrich
L -抗坏血酸, puriss. p.a., ≥99.0% (RT)
D8284
Sigma-Aldrich
二喹啉甲酸 二钠盐 水合物, ≥98% (HPLC)
SML0332
Sigma-Aldrich
依地芬, ≥95% (HPLC)