Controllable synthesis of Cu2O/Cu composites with stable photocatalytic properties.

Controllable synthesis of Cu2O/Cu composites with stable photocatalytic properties.

Journal of nanoscience and nanotechnology (2014-04-18)

Xueqin Liu, Fei Li, Huifang Wang, Jianbo Yang, Zhen Li, Yongqian Wang, Hongyun Jin

摘要

Here we reported a facile approach to synthesize Cu2O/Cu composite particles by one-step sono-chemical process. The content of Cu in the Cu2O/Cu composites can be easily controlled by adjusting the synthesis time. Phase, morphology and optical properties of the products were carried out by X-ray diffraction (XRD), field-emission scanning electron microscopy (FSEM), transmission electron microscope (TEM), ultraviolet-visible (UV-vis) spectroscopy and nitrogen adsorption apparatus. Using photocatalytic degradation of Methyl orange (MeO) dye under visible-light illumination, we have investigated the influence of Cu on the photocatalytic activity of Cu2O, to find out its potential application in waste water treatment. Especially, the stability of the photocatalyst was confirmed using reclaimed Cu2O/Cu in ten successive runs. Results demonstrated clearly that Cu2O/Cu were stable and resistant to photocorrosion during the photocatalytic oxidation of organic compounds, indicating that these Cu2O/Cu composites are promising candidates for pollutant processing.

材料

产品编号

品牌

产品描述

Sigma-Aldrich

氧化铜, ACS reagent, ≥99.0%

Sigma-Aldrich

氧化铜, nanopowder, <50 nm particle size (TEM)

Sigma-Aldrich

甲基橙, ACS reagent, Dye content 85 %

Sigma-Aldrich

氧化铜, powder, <10 μm, 98%

Sigma-Aldrich

铜, powder, <425 μm, 99.5% trace metals basis

Sigma-Aldrich

铜, foil, thickness 0.25 mm, 99.98% trace metals basis

Sigma-Aldrich

铜, powder, 99.99% trace metals basis

Sigma-Aldrich

甲基橙, suitable for microscopy

Sigma-Aldrich

铜, powder, <75 μm, 99%

Sigma-Aldrich

铜, wire, diam. 1.0 mm, ≥99.9%

Sigma-Aldrich

铜, nanopowder, 40-60 nm particle size (SAXS), ≥99.5% trace metals basis

Sigma-Aldrich

氧化铜, powder, 99.99% trace metals basis

Sigma-Aldrich

铜, powder (spheroidal), 10-25 μm, 98%

Sigma-Aldrich

铜, powder (dendritic), <45 μm, 99.7% trace metals basis

Sigma-Aldrich

铜, foil, thickness 0.025 mm, 99.98% trace metals basis

Sigma-Aldrich

铝基氧化铜, 14-30 mesh, extent of labeling: 13 wt. % loading

Sigma-Aldrich

氧化铜, needles, mixture of CuO and Cu₂O, ACS reagent

Sigma-Aldrich

铜, turnings, purum p.a., ≥99.0%

Sigma-Aldrich

铜, nanopowder, 60-80 nm particle size (APS), ≥99.5% trace metals basis

Sigma-Aldrich

铜, ACS reagent, granular, 10-40 mesh, ≥99.90%

Sigma-Aldrich

铜, beads, 2-8 mm, 99.9995% trace metals basis

Sigma-Aldrich

铜, foil, ≥99.8% (complexometric)

Sigma-Aldrich

铜, foil, thickness 1.0 mm, 99.999% trace metals basis

铜, mesh, 100x100mm, nominal aperture 0.14mm, thickness 0.25mm, wire diameter 0.115mm, 100x100 wires/inch, open area 30.3%, plain weave mesh

Sigma-Aldrich

铜, foil, thickness 0.5 mm, 99.98% trace metals basis

Sigma-Aldrich

氧化铜, 99.999% trace metals basis

Sigma-Aldrich

铜, wire, diam. 0.25 mm, 99.999% trace metals basis

Sigma-Aldrich

铜, shot, −3-+14 mesh, 99%

Sigma-Aldrich

铜, beads, 2-8 mm, ≥99.99% trace metals basis

Sigma-Aldrich

氧化铜, powder, 99.995% trace metals basis